BC 701 Spray 15
Product Description:-
.
.
BC 701 Spray 15, spray polyurethane open-cell foam system (SPF) for and thermal
and acoustic (Noise /Sound proof insulation applications ) and is specifically
formulated to apply low-density foam (±8~12 kg/m³),
Its application must be carried out by the specific reactor equipment by mixing BC
701 Spray 15 (polyol side) and BC 768 isocyanate. (Isocyanate side )
The blowing agent is water.
The spray polyurethane foam system BC 701 Spray 15 can be used in these
situations:
Application continuous thermal insulation systems in residential buildings, businesses
or industries
Indoor applications ceilings, interior chambers facade, ventilated facades, internal
side of roofs, made with wood structure, or other material (see compatibility)
Uses:
General Features:
Applied density ± 8~12 kg/m³
Thermal conductivity 0,039 W/m·K
Cream time 4~8 secs
Gel time 8~13 secs
Tack-free time 13~17 secs
BC 701 Spray 15 is an open cell SPF, for thermal and acoustic insulatinon,easy
to apply and to protect all the internal surfaces of the building
The properties of the polyurethane foam system BC 701 Spray 15 allow it to
adhere to any surface such as concrete, ceramic, metal, polyurethane foam,
wood, acrylic paints (checking the situation of areas recommended).
It forms a continuous coat without joints preventing the formation of "heat
bridges" and providing an optimum thermal insulation surface with high
thermal insulation parameters
As the blowing agent is water. It is free from harmful to the ozone layer, so do
not promote the greenhouse effect
(NOT contain HFCs, HCFCs, VOCs, etc ...); it does not emit any substance to
the environment once installed.
The applied system is 100% recyclable by mechanical means friendly to the
environment. No gas collection for recycling and/or destruction is required
The thermal conductivity coefficient remains unchanged from the application and along with
the product life.
Building Chemistry Industry
Suit No 203, Al Manar Business park Bin Khalid Street Dammam .Kingdom of Saudi Arabia.
Email: info@bcisaudi.com Website: www.bcisaudi.com
Metal drums of 220 kg for the polyol, and 250 kg for the isocyanate.
Packaging:
12 months
Temperature within 5 ºC ~ 35 ºC, provided it is stored in a dry place, with no direct
contact with the sun.
These safety recommendations for handling, are necessary for the implementation
process as well as in the pre-andpost, on exposure to the loading machinery.
Respiratory Protection: When handling or spraying use an air-purifying respirator.
Skin protection: Use rubber gloves, remove immediately after contamination. Wear clean
body-covering. Wash thoroughly with soap and water after work and before eating,
drinking, or smoking.
Eye / Face: Wear safety goggles to prevent splashing and exposure to particles in the air.
Waste: Waste generation should be avoided or minimized.
Shelf Life:
Application Method:
Handling:
The application of polyurethane foam system BC 701 Spray 15 should be
performed under non-presence of moisture or water from the support stand
on which to apply either at the time of application
The substrate must be clean and free of dust
In applications with high-temperature gradients a vapor barrier is placed on
the warm side of the insulation to prevent condensation
Metal surfaces should be protected with an anti-corrosive primer before being
coated with foam. On smooth surfaces without pores, galvanized steel,
polypropylene, etc ... a secure grip primer should be applied
To apply in one direction to achieve the expansion which is about 10 ~ 12 cm.
per coat.
If necessary, and once fully expanded, apply a second layer on the already
initially applied.
Its great expansion causes sometimes have to cut the excess with the help of
a saw
BC 701 Spray 15 adheres firmly to most common materials such as wood,
plasterboard, steel, OSB plywood, cement, inside masonry exterior plaster
panels, and construction itself.,
Building Chemistry Industry
Suit No 203, Al Manar Business park Bin Khalid Street Dammam .Kingdom of Saudi Arabia.
Email: info@bcisaudi.com Website: www.bcisaudi.com
Compound Characteristics:
Characteristic Value:
Characteristic
Polyol
Isocyanate
(MDI)
Brookfield Viscosity
290mPa.s
210 mPa.s
NCO content ISO 14896
31%
Specific gravity
1,09
g/cm³
1,23 g/cm³
Mix ratio by volume
100
100
Mix ratio by weight
100
113
Cream time 4~8 secs
Gel time 8~13 secs
Tack-free time 13~17 secs
Density free rise 8 kg/m³
Closed-cell content ASTM 2856 <15% (CCC1)
Thermal conductivity value EN-12667 0,039 W/mK
Tensile strength perpendicular to face EN-1607:2013 8,4 kPa
Dimensional stability (-20ºC/-%) EN-1604:2013 0,0|0,1|0,1 %
Dimensional stability (70ºC/ 90%) EN-1604:2013 -2,8|-2,3|0,8 %
VOC (volatile organic compounds ) ISO 16000-6 Class A+aC
Acoustic test -40db in 195mm (thickness)